Ordered mesoporous carbons with fiber-and rod-like morphologies for supercapacitor electrode materials

作者:Xiao Yong; Dong Hanwu; Lei Bingfu; Qiu Huihua; Liu Yingliang*; Zheng Mingtao
来源:Materials Letters, 2015, 138: 37-40.
DOI:10.1016/j.matlet.2014.09.090

摘要

The ordered mesoporous carbons (OMCs) with fiber like and rod like morphologies were selectively synthesized through a simple method and their electrochemical properties has been investigated. The conventional fiber-like SBA-15 was employed as hard template and sucrose as carbon precursor. When the infiltration process under static conditions or stirring for 24 h, the result carbons exhibited fiber-like (OMC-1) or rod-like (OMC-2) morphologies, respectively. Detailed characterizations of the samples revealed that, though the BET surface areas and pore volumes of OMC-2 (1217 m(2)/g and 1.23 m(3)/g, respectively) were slightly lower than those of OMC-1 (1358 m(2)/g and 1.53 m(3)/g, respectively), the electrochemical behavior of OMC-2 was abnormally better than OMC-1. The specific gravimetric capacitance was 162 F/g at a scan rate of 2 mV/s and the retained ratio was 82% at 50 mV/s for OMC-2, which was 151 F/g and 79% for OMC-1, respectively. Therefore, the as-prepared carbon, especially OMC-2 can be a potential candidate for supercapacitors.

  • 单位
    华南农业大学

全文