Oxygen Doping in Graphitic Carbon Nitride for Enhanced Photocatalytic Hydrogen Evolution

作者：Huang, Jiangnan; Wang, Hongjuan; Yu, Hao; Zhang, Qiao; Cao, Yonghai^*; Peng, Feng^*

来源：ChemSusChem, 2020, 13(18): 5041-5049.

DOI：10.1002/cssc.202001317

• photocatalysis
• hydrogen production
• graphitic carbon nitride
• surface oxygen groups
• charge separation

The incorporation of oxygenic groups could remarkably enhance the light absorption and charge separation of graphitic carbon nitride (g-C3N4). The intrinsic role of oxygenic species on photocatalytic activity in g-C(3)N(4)has been intensively studied, but it is still not fully explored. Herein, the essential relationships between oxygenic functionalities and the catalytic performance are revealed. Results demonstrate that C-O-C functionality as an electron trap could help to increase the resistance of conduction transfer (R-ct) by limiting electrons transfer in CNx. In contrast, N-C-O functionality between different tri-s-triazine unites could promote the electrons transfer, leading to a reducedR(ct)in CNx. The best H(2)production rate (3.70 mmol h(-1) g(-1), 12.76-fold higher than that of CN) is obtained over CN3, because of the highest N-C-O ratio (r(N-C-O)). The apparent quantum efficiency (AQE) of CN3 at 405 nm, 420 nm, 450 nm, 500 nm and 550 nm is 33.90 %, 20.88 %, 8.25 %, 3.66 % and 1.01 %, respectively.

• 单位
  广州大学