3D-printed strontium-doped BG-CaSiO3-HA composite scaffolds promote critical bone defect repair by improving mechanical strength and increasing osteogenic activity

Authors：Dai, Kun; Yang, Zhen; Ding, Lin; Yang, Zhengyu; Hang, Fei; Cao, Xiaodong; Chen, Dafu; Zhao, Fujian^*; Chen, Xiaofeng^*

Source：Ceramics International, 2023, 49(12): 19773-19785.

DOI：10.1016/j.ceramint.2023.03.095

• Bioglass
• 3D printing
• Ceramic
• CaSiO3

The release of silicon and calcium elements contained in silicon-based materials promotes the formation of bone. For bioactive glass prepared by the sol-gel method, water-soluble binders are usually added when preparing 3D printed scaffolds. However, the obtained scaffolds are prone to collapse when exposed to water and have low strength. At the same time, the binder needs to be removed for clinical applications, so the 3D printed scaffolds need to be sintered. Under high temperature, bioactive glass scaffolds will be transformed into composite scaffolds composed of bioglass, CaSiO3 and hydroxyapatite, while different sintering temperatures will form different crystal types of CaSiO3. In this study, SrBG-beta CS-HA and BG-beta CS-HA were obtained at a heating rate of 5 degrees C/min to 1100 degrees C and at the same rate to room temperature. SrBG-alpha CS-HA and BG-alpha CS-HA were obtained at a heating rate of 2 degrees C/min to 1200 degrees C and at the same rate to room temperature. In vitro and in vivo experiments verified that the presence of strontium in the obtained scaffolds after sintering further enhanced the osteogenic properties of the scaffolds. SrBG-alpha CaSiO3-HA and SrBG-beta CaSiO3-HA were found to have relatively better oste-ogenic properties. The results show that SrBG-CaSiO3-HA 3D printing scaffolds have excellent clinical application potential.

• Institution
  南方医科大学