Experimental study and numerical simulation of infiltration of AlSi12 alloys into Si porous preforms with micro-computed tomography inspection characteristics

摘要

Silicon particle preforms with different starch contents (10, 20 and 30%) and particle sizes (20, 50 and 90 mu m) were fabricated by compression mold forming and heat treatment. The pore characteristics of preforms were inspected with a high-resolution (similar to 1 mu m) three-dimensional (3D) X-ray micro-computed tomography (mu-CT). The infiltration of AlSi12 alloys into the preforms were carried out under the condition of 800 degrees C and 400 kPa with different pressure-applied times (3, 8 and 15 s) in a vacuum-assisted pressure infiltration apparatus. A high-resolution (similar to 500 nm) vertical scanning white light interfering profilometer was used to detect the front surfaces of composites. The infiltration was simulated at micro-scale by considering the actual pore geometry from the mu-CT inspection based on the Navier-Stokes equation. The results demonstrated that as the starch content and particle size increased, the front surface area of composite increased. Compared with the starch content, the particle size has more influence on the front surface area. In the simulation, as the infiltration progressed, the pressure of liquid AlSi12 decreased. The residual pores of composites increased with infiltration. According to the experiment and simulation results, a larger pressure drop along the infiltration direction leads to more residual pores of composites.

关键词