An ultrahigh-areal-capacity SiOx negative electrode for lithium ion batteries

摘要

Constructing a stable microstructure is highly crucial in promoting the practical applications of Si-based negative electrodes, addressing the issues of huge volume change and unstable solid electrolyte interface (SEI). Herein, an integrated electrode structure is developed based on micro-sized SiOx particles by bilayers coating of carbon and poly(3,4-ethylene dioxythiophene) (PEDOT) with carbon nanotube/Super P conductive network in-situ embedded (SiOx@C@P_CS). The as-prepared SiOx@C@P_CS negative electrode exhibits high Coulombic efficiency reaching 99.9% and capacity retentions of 86.7% (1019 mAh g(-1)) after 1000 cycles at 750 mA g(-1) and 98.4% (973 mAh g(-1)) after 400 cycles at 1500 mA g(-1) (with a commercial-level areal capacity of 2.57 mAh cm(-2)). The excellent long cycling capability is further evidenced both in half cell with ultrahigh areal capacity up to 11.75 mAh cm 2 at the mass loading of 8.66 mg cm(-2) and Li[Ni0.8Co0.1Mn0.1]O-2 (NCM811)parallel to SiOx@C@P_CS full cell with commercial loading. The improved electrochemical performance is attributed to the synergistic effects of the bilayers. This study offers a facile solution to the challenges facing alloying-type negative electrode materials with huge volume changes by confining volume change, enhancing electric conductivity, and isolating the growth of SEI to promote their practical uses.

关键词