Annealing-Insensitive, Alcohol-Processed MoOx Hole Transport Layer for Universally Enabling High-Performance Conventional and Inverted Organic Solar Cells

摘要

At present, most solution-processed molybdenum oxide (s-MoOx) hole transport layers (HTLs) are still mainly used in conventional organic solar cells (OSCs) but unsuitable for inverted OSCs. Herein, we demonstrate for the first time an annealing-insensitive, alcohol-processed MoOx HTL that can universally enable high-performance conventional and inverted OSCs. The s-MoOx HTL is spin-coated from the MoOx; nanoparticle dispersion in alcohol, where the MoOx nanoparticles are synthesized by simple nonaqueous pyrolysis conversion of MoO2(acac)(2). The MoOx nanoparticles possess uniform and very small sizes of less than 5 nm and can be well dispersed in alcohol, so the s-MoOx HTLs on ITO and active layer both show an overall uniform and smooth surface, suitable for conventional and inverted OSCs. In addition, the s-MoOx HTL possesses decent optical transmittance and appropriate work function. Utilizing the s-MoOx HTL annealed between room temperature and 110 degrees C and PM6:Y6 active layer, the conventional OSCs show an excellent power conversion efficiency (PCE) of 16.64-17.09% and the inverted OSCs also show an excellent PCE of 15.74-16.28%, which indicate that the s-MoOx HTL could be annealing-insensitive and universal for conventional and inverted OSCs. Moreover, conventional and inverted OSCs with the s-MoOx HTLs annealed at 80 degrees C both exhibit optimal PCEs of 17.09 and 16.28%, respectively, which are separately superior than that of the PEDOT:PSS-based conventional OSCs (16.94%) and the thermally evaporated MoO3 (e-MoO3)-based inverted OSCs (16.03%). Under light soaking and storage aging in air, the unencapsulated inverted OSCs based on the s-MoOx HTL show similarly excellent ambient stability compared to the e-MoOx-based devices. In addition, the s-MoOx HTL also shows a universal function in conventional and inverted OSCs with PBDB-T:ITIC and PM6:L8-BO active layers. Notably, the s-MoOx-based conventional and inverted OSCs with the PM6:L8-BO active layer exhibit very excellent PCEs of 18.21 and 17.12%, respectively, which are slightly higher than those of the corresponding PEDOT:PSS-based device (18.17%) and e-MoO3-based device (17.00%). The annealing-insensitive, alcohol-processed MoOx HTL may be very promising for flexible and large-scale processing conventional/inverted OSCs.

关键词