Diffusivity, solubility and thermodynamic modelling of diffusion growth of Ga3+-doped LiTaO3 thin film for integrated optics

Authors：Zhang D L^*; Zhang Q; Zhang P; Kang J; Wong W H; Yu D Y; Pun E Y B

Source：Journal of Chemical Thermodynamics, 2016, 97: 93-99.

DOI：10.1016/j.jct.2015.11.001

• Ga3+ diffusion growth
• LiTaO3
• Thermodynamic properties

A thermodynamic study was performed on diffusion growth of Ga3+-doped LiTaO3(LT) thin film for integrated optics. Some Ga3+-doped LT thin films were grown on LT surface by in-diffusion of homogeneously coated Ga2O3 film at the temperature range of (1273 to 1473) K. After growth, the refractive indices at Ga3+-doped and un-doped surface parts were measured by prism coupling technique and Li composition there was evaluated from the measured refractive indices. The results show that Ga3+ dopant has small effect on the LT index. Li2O out-diffusion is not measurable. The Ga3+ profile in the grown thin film was analysed by secondary ion mass spectrometry. It is found that the grown Ga3+ ions follow a complementary error function profile. A thermodynamic model for Ga3+ diffusion growth is suggested and verified experimentally. From the measured Ga3+ profiles, some thermodynamic parameters were obtained. These include diffusivity, diffusion constant, chemical activation energy, solubility, solubility constant and enthalpy of solution. These parameters are crucial to design and growth of a desired Ga3+-doped LT thin film for integrated optics. Comparison shows that Ga3+ grows in LT two orders faster than Ti4+ because of its smaller radius. Ga3+ diffusivity/solubility in LT is one order/1.5-fold lower than in LiNbO3 because Ta has a larger atomic mass and hence a lower mobility than Nb.

• Institution
  2