Enhanced ethopabate adsorption in monodispersed porous carbon derived from zeolitic imidazolate framework-8

Authors：Hu, Haoyun; Ruan, Guihua^*; Jiang, Xiangqiong; Pan, Hong; Wu, Zhuqiang; Huang, Yipeng^*

Source：New Journal of Chemistry, 2022, 46(17): 8224-8231.

DOI：10.1039/d2nj00843b

• METAL-ORGANIC FRAMEWORKS
• NANOPOROUS CARBON
• ZIF-8
• CARBONIZATION
• TEMPERATURE
• CO2

The improvement of the adsorption performance of adsorbents to the target substance plays a crucial role in the actual sample pretreatment. Here, a convenient, sustainable and efficient strategy was developed for the fabrication of the monodispersed porous carbon material. It was derived from the direct carbonization of zeolitic imidazolate framework-8 (ZIF-8) with controllable pore size and uniform morphology without any additional carbon source. The Brunauer-Emmett-Teller (BET) surface area of carbonized ZIF-8 (C/ZIF-8) was as high as 1463.20 m(2) g(-1) and pore volume was 0.5608 cm(3) g(-1), and the adsorption capacity of the C/ZIF-8-based solid phase extraction (SPE) column greatly enhanced to 640.88 mu g g(-1) compared with the adsorption capacity (93.36 mu g g(-1)) of original ZIF-8 towards ethopabate (ETP), achieving an improvement of about 7 times. Highly efficient ETP extraction was achieved with C/ZIF-8 under pH 3.0-7.0 for 16 min, and nearly 100% desorption efficiency was obtained when eluted with methanol for 12 min. The ETP enrichment on C/ZIF-8 and coupled with the high performance liquid chromatography (HPLC) detection provided a feasible method for the analysis of ETP in chicken samples. The recovery and the relative standard deviation of the method were 89.66-99.58% and 0.31-1.77%, respectively.

• Institution
  桂林理工大学