Bi0.5Na0.5TiO3-based relaxor-ferroelectric ceramics for low-electric-field dielectric energy storage via bidirectional optimization strategy

作者：Wang, Qi; Xie, Bing^*; Zheng, Qiuyu; Marwat, Mohsin Ali; Liu, Zhiyong; Mao, Pu; Jiang, Shenglin; Zhang, Haibo

来源：Chemical Engineering Journal, 2023, 452: 139422.

DOI：10.1016/j.cej.2022.139422

• Ion pair
• Domain engineering
• Relaxor ferroelectrics
• Energy storage

Dielectric ceramics for electrostatic energy storage suffer from low recoverable-energy-density (Wrec) at a low -electric-field (LEF), constraining their use in downsizing integrated electronic devices and low operating voltage environments. Here, we report a 0.85Bi0.5Na0.5TiO3-0.15(Sr0.7Bi0.2)(Mg1/3Nb2/3)O3 (0.85BNT-0.15SBMN) relaxor ferroelectric ceramic that exhibits a high Wrec of 3.6 J/cm3 at a LEF of 200 kV/cm. This Wrec is among one of the highest under the equivalent applied electric field for relaxor ferroelectrics re-ported so far. It is revealed that the construction of Sr2+-Sr2+ ion pairs to replace the pristine Bi3+-Na+ ion pairs and the introduction of SBMN yield a high concentration of Bi3+ at the A-site, leading to high polarization (52.4 mu C/cm2 at 200 kV/cm). Additionally, the newly introduced Mg2+ and Nb5+ at the B-site to replace the host Ti4+ causes local random fields (LRFs) that disrupt the long-range-ordered ferroelectric micro-domains, leading to the generation of the polar nanoregions with favorable relaxation properties. Above bidirectional optimization strategy leads to substantial Wrec improvements at a LEF. Furthermore, the variation of Wrec is less than 0.4 J/ cm3 and 0.5 J/cm3 in a wide frequency (10 Hz-1000 Hz) and temperature (20 to 120 degrees C) range, indicating a good frequency and thermal stability. This finding provides a new guideline for fabricating LEF dielectric energy storage ceramics.

• 单位
  南昌航空大学; 华中科技大学