The mixture of silver nanowires and nanosilver-coated copper micronflakes for electrically conductive adhesives to achieve high electrical conductivity with low percolation threshold

作者：Qian Wang; Shuye Zhang; Guiming Liu; Tiesong Lin; Peng He

来源：Journal of Alloys and Compounds, 2019, 153184.

DOI：10.1016/j.jallcom.2019.153184

• Silver nanowires
• Nanosilver-coated copper micronflakes
• Electrical conductivity
• Percolation threshold
• Electrically conductive adhesives

For electrically conductive adhesives (ECAs), it is critical to ensure high electrical conductivity and good adhesion reliability for practical applications in electronic products. In this study, high conductivity ECAs at low filler content were achieved by fully utilizing the synergistic effect of nano- and micro-scale fillers. Nanosilver-coated copper micronflakes ([email protected]) prepared by an electroless plating method were selected as the main conductive fillers. Silver nanowires (AgNWs) made by a simple one-step polyol method were dispersed as auxiliary conductive fillers in [email protected], providing more possibilities for establishing a large number of conductive bridges. Furthermore, the curing process of matrix resin was predicted based on curing kinetics and was verified by corresponding experiments to determine the optimal curing parameters. The results show that the combination of AgNWs and [email protected] in ECAs can significantly reduce the bulk resistivity and percolation threshold compared with the single component. In particular, the bulk resistivity of ECAs filled with AgNWs and [email protected] (mass ratio 1:9) is as low as 9.42 × 10−5 Ω cm when the filler content is only 60 wt%.